Effect of chlorhexidine and isopropyl alcohol on immediate and delayed bond strength of glass fiber posts


Published: 31 October 2019
Abstract Views: 831
pdf: 471
Publisher's note
All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article or claim that may be made by its manufacturer is not guaranteed or endorsed by the publisher.

Authors

Aim: To investigate the effects of dentinal treatment with chlorhexidine and isopropyl alcohol, alone or associated, on the bond strength and bond stability of glass fiber posts cemented with a self-adhesive resin cement.

Materials and Methods: Forty bovine teeth were endodontically treated and randomly distributed into four groups, according to the dentinal treatment after post space preparation: distilled water (Control); 2% chlorhexidine (CHX); isopropyl alcohol (ISO); 2% chlorhexidine + isopropyl alcohol (CHX+ISO). Glass fiber posts were cemented with a self-adhesive resin cement and after 24 h specimens were cut into six 1.5 mm-thick slices. One slice of each root third (i.e. apical, middle and coronal) was subjected to immediate push-out test and the other was stored in distilled water at 37 °C for six months for delayed push-out test. Bond strength was registered in megapascal (MPa). Failure mode was evaluated by a stereomicroscope, with 40x magnification. Data analysis was performed using Kruskal-Wallis and Friedman tests, with 5% significance level. Results: No significant differences were detected between experimental groups or between root thirds in the same group in the immediate evaluation. After six months of aging, all groups showed a significant decrease in bond strength values, but ISO group presented higher bond strength than Control and CHX groups (p=0.0001). The most common type of failure for all groups was adhesive between resin cement and root dentine.

Conclusions: Dentinal treatment with CHX and ISO, isolated or combined, did not affect the immediate bond strength of glass fiber posts, but the ISO group presented better bond stability after six-month aging.


Anater Lecardelli, E. ., Poletto-Neto, V. ., Pappen, F. G. ., Pereira-Cenci, T. ., & Dornelles Morgental, R. . (2019). Effect of chlorhexidine and isopropyl alcohol on immediate and delayed bond strength of glass fiber posts. Giornale Italiano Di Endodonzia, 33(2). https://doi.org/10.32067/gie.2019.33.02.06